PA66 A 205F BLACK 21 N法國羅地亞TECHNYL連接器緊固件束線帶用尼龍66塑料（18024445500）

TECHNYL A 205F BLACK 21 N 　 　 　 　
　 　 　 Properties 　
　 Typical values of properties are for natural grades
　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 1,20 　
Density ISO 1183/A g/cm3 1,14 　
Molding shrinkage Parallel RHODIA % 1,90 　
Molding shrinkage normal or perpendicular RHODIA % 1,90 　
Molding Shrinkage Isotropy RHODIA 　 1　　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 3200　1400　
Tensile strength at yield ISO 527 Type 1A MPa 85　50　
　 ASTM D-638 MPa 85　　
Tensile strength at break ISO 527 Type 1A MPa 60　40　
Elongation at yield ISO 527 Type 1A % 4　10　
Elongation at break ISO 527 Type 1A % 50　250　
　 ASTM D-638 % 25　　
Flexural modulus ISO 178 MPa 3000　1300　
　 ASTM D-790 MPa 3350　　
Flexural maximum stress ISO 178 MPa 120　50　
　 ASTM D-790 MPa 125　　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 5　10　
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 NB NB
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 5　8　
　 ASTM D256 J/m 80　　
Flammability 　 　 　 　
Flammability (Thickness: 0,4 mm) ISO 1210 / UL94 　 V2 　
Flammability (Thickness: 0,8 mm) ISO 1210 / UL94 　 V2 　
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 　 V2 　
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 850　　
Limit Oxygen Index ISO 4589 　 29　　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 75　　
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 7　　
perpendicular (23°C to 85°C) 　 　 　 　
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 7　　
85°C) 　 　 　 　
Electrical 　 　 　 　
Comparative tracking index (Sol A) IEC 60112 V 600　600　
Comparative tracking index (Sol B) IEC 60112 V 550　　
Dielectric strength IEC 60243 kV/mm 27　26　
Dissipation factor IEC 60250 　 0,030 0,080
Relative permittivity IEC 60250 　 2,90 3,20
Surface resistivity IEC 60093 Ohm 5E 14 1E 13
Volume resistivity IEC 60093 Ohm/cm 1E 15 1E 13