PA66 A 218 V50 BLACK 21 N法國羅地亞TECHNYL 50%玻纖增強熱穩定尼龍66塑料（18024445500）









TECHNYL A 218 V50 BLACK 21 N 　 　 　 　
　 　 　 Properties
　 Typical values of properties are for natural grades
　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 0,60 　
Density ISO 1183/A g/cm3 1,57 　
Molding shrinkage Parallel RHODIA % 0,44 　
Molding shrinkage normal or perpendicular RHODIA % 0,80 　
Molding Shrinkage Isotropy RHODIA 　 0,55 　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 16200　12500　
Tensile strength at break ISO 527 Type 1A MPa 240　175　
　 ASTM D-638 MPa 220　　
Elongation at break ISO 527 Type 1A % 2　3　
Flexural modulus ISO 178 MPa 13500　10000　
　 ASTM D-790 MPa 13800　　
Flexural maximum stress ASTM D-790 MPa 350　　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 16　18　
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 95　97　
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 14,5 17　
　 ASTM D256 J/m 180　　
Flammability 　 　 　 　
Flammability (Thickness: 0,8 mm) ISO 1210 / UL94 　 HB 　
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 　 HB 　
Flammability (Thickness: 3,2 mm) ISO 1210 / UL94 　 HB 　
Glow Wire Flammability Index (Thickness: 0,8 mm) ISO 60695-2-12 °C 650　　
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 650　　
Glow Wire Flammability Index (Thickness: 3,2 mm) ISO 60695-2-12 °C 700　　
Limit Oxygen Index ISO 4589 　 23　　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 255　　
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 255　　
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 1,5 　
85°C) 　 　 　 　
Electrical 　 　 　 　
Comparative tracking index (Sol A) IEC 60112 V 600　600　
Dielectric strength IEC 60243 kV/mm 35　30　
Dissipation factor IEC 60250 　 0,010 0,110
Relative permittivity IEC 60250 　 3,70 4　
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 1E 15 1E 13