PA6 PX09322沙伯基礎創新LNP™ KONDUIT™ PX09322 compound白色導熱礦物填充（18024445500）

General Information
Product Description
White colored thermally conductive mineral filled PA6 FR compound
General　
Material Status　Commercial: Active

Availability　Asia Pacific

Filler / Reinforcement　Mineral

Features　Flame Retardant
Thermally Conductive
　

Appearance　White

Processing Method　Injection Molding


ASTM & ISO Properties 1
Physical Nominal Value Unit Test Method
Density 1.52 g/cm³ ASTM D792
Molding Shrinkage - Flow　5.8E-3 in/in Internal Method
Molding Shrinkage - Across Flow　5.3E-3 in/in Internal Method
Water Absorption (24 hr, 50% RH) 0.060 % ASTM D570
UV Weathering - Start F1 from 1mm onword　PASSES　UL 746C
Water Immersion - Start F1 from 1mm onword　PASSES　UL 746C
Mechanical Nominal Value Unit Test Method
Tensile Modulus 2 1.51E+6 psi ASTM D638
Tensile Strength 3 (Break) 7400 psi ASTM D638
Tensile Elongation 3 (Break) 0.80 % ASTM D638
Flexural Modulus 4 (1.97 in Span) 1.59E+6 psi ASTM D790
Flexural Strength 4 (Yield, 1.97 in Span) 11600 psi ASTM D790
Flexural Strength 4 (Break, 1.97 in Span) 11700 psi ASTM D790
Impact Nominal Value Unit Test Method
Notched Izod Impact (73°F) 0.41 ft·lb/in ASTM D256
Unnotched Izod Impact (73°F) 2.5 ft·lb/in ASTM D4812
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load (66 psi, Unannealed, 0.252 in) 410 °F ASTM D648
Deflection Temperature Under Load (264 psi, Unannealed, 0.252 in) 360 °F ASTM D648
CLTE - Flow (-40 to 104°F) 1.3E-5 in/in/°F ASTM E831
CLTE - Transverse (-40 to 104°F) 2.0E-5 in/in/°F ASTM E831
Thermal Conductivity　 ASTM E1461
-- 5 10 Btu·in/hr/ft²/°F　
-- 6 42 Btu·in/hr/ft²/°F　
Thermal Conductivity　 ISO 22007-2
-- 7 6.0 Btu·in/hr/ft²/°F　
-- 8 19 Btu·in/hr/ft²/°F　
Electrical Nominal Value Unit Test Method
Surface Resistivity 8.1E+14 ohm ASTM D257
Comparative Tracking Index (CTI) PLC 0　UL 746
Flammability Nominal Value Unit Test Method
Flame Rating (0.0472 in) V-0　UL 94
Glow Wire Flammability Index (0.0394 in) 1760 °F IEC 60695-2-12

Processing Information
Injection Nominal Value Unit　
Drying Temperature 176 to 194 °F　
Drying Time 3.0 to 4.0 hr　
Suggested Max Moisture 0.010 %　
Rear Temperature 446 to 518 °F　
Middle Temperature 464 to 536 °F　
Front Temperature 482 to 536 °F　
Nozzle Temperature 482 to 536 °F　
Processing (Melt) Temp 482 to 536 °F　
Mold Temperature 176 to 212 °F　
Back Pressure 435 to 1310 psi　
Screw Speed 30 to 150 rpm　

Notes
1Typical properties: these are not to be construed as specifications.
22.0 in/min
3Type I, 0.20 in/min
40.051 in/min
5through-plane, 10*10*3mm sample
6in-plane, ø25*0.4mm disc
7through-plane, ø80*3mm discs
8in-plane, ø80*3mm discs