PA66 70G43L NC010美國杜邦Zytel® 43%玻璃纖維增強(qiáng)聚酰胺66塑料（18024445500）

Zytel® 70G43L NC010 is a 43% glass fiber reinforced polyamide 66 resin for injection moulding.
General information Value Unit Test Standard
Resin Identification PA66-GF43 - -
Part Marking Code >PA66-GF43< - ISO 11469
Rheological properties dry / cond Unit Test Standard
Viscosity number 130 / * cm³/g ISO 307, 1157, 1628
Moulding shrinkage, parallel 0.3 / * % ISO 294-4, 2577
Moulding shrinkage, normal 1.0 / * % ISO 294-4, 2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 14000 / 11000 MPa ISO 527-1/-2
Stress at break 225 / 160 MPa ISO 527-1/-2
Strain at break 3 / 4 % ISO 527-1/-2
Flexural Modulus 12000 / 8900 MPa ISO 178
Flexural Strength 340 / 260 MPa ISO 178
Tensile creep modulus 　 　 ISO 899-1
1h * / 10800 MPa 　
1000h * / 7960 MPa 　
Charpy impact strength 　 　 ISO 179/1eU
23°C 100 / 105 kJ/m² 　
-30°C 85 / 75 kJ/m² 　
Charpy notched impact strength 　 　 ISO 179/1eA
23°C 16 / 19 kJ/m² 　
-30°C 12 / 12 kJ/m² 　
-40°C 11 / 11 kJ/m² 　
Izod notched impact strength 　 　 ISO 180/1A
23°C 14 / 16 kJ/m² 　
-30°C 12 / 11 kJ/m² 　
-40°C 11 / 11 kJ/m² 　
Izod impact strength 　 　 ISO 180/1U
23°C 105/90 kJ/m² 　
-30°C 105/65 kJ/m² 　
Hardness, Rockwell, M-scale 105/90 - ISO 2039-2
Hardness, Rockwell, R-scale 125/118 - ISO 2039-2
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 262/* °C ISO 11357-1/-3
Glass transition temperature, 10°C/min 80/- °C ISO 11357-1/-2
Temp. of deflection under load 　 　 ISO 75-1/-2
1.8 MPa 255/* °C 　
0.45 MPa 262/* °C 　
Vicat softening temperature, 50°C/h, 50N 255/* °C ISO 306
Coeff. of linear therm. expansion, parallel 15/* E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 79/* E-6/K ISO 11359-1/-2
Thermal conductivity of melt 0.25　W/(m K) -
Spec. heat capacity of melt 2050　J/(kg K) -
RTI, electrical, 0.75 mm 130 / * °C UL 746B
RTI, impact, 0.75 mm 120　°C UL 746B
RTI, strength, 0.75 mm 130　°C UL 746B
Flammability dry / cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. HB / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
UL recognition UL / * - -
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 0.71 / * mm IEC 60695-11-10
Oxygen index 23 / * % ISO 4589-1/-2
Glow Wire Flammability Index 　 　 IEC 60695-2-1/2
0.75mm 650 / - °C 　
1.5mm 650 / - °C 　
3mm 825 / - °C 　
Glow Wire Ignition Temperature 　 　 IEC 60695-2-1/3
0.75mm 675 / - °C 　
1.5mm 675 / - °C 　
3mm 700 / - °C 　
Burning rate, Thickness 1 mm 27　mm/min ISO 3795 (FMVSS 302)
Electrical properties dry / cond Unit Test Standard
Relative permittivity 　 　 IEC 60250
100Hz 4.5 / - - 　
1MHz 4.1 / 4.9 - 　
Dissipation factor 　 　 IEC 60250
100Hz 100 / - E-4 　
1MHz 145 / 600 E-4 　
Volume resistivity >1E13 / 1E10 Ohm*m IEC 60093
Surface resistivity * / 1E12 Ohm IEC 60093
Electric strength 27 / - kV/mm IEC 60243-1
Electric Strength, Short Time, 2mm 27 / - kV/mm IEC 60243-1
Other properties dry / cond Unit Test Standard
Humidity absorption, 2mm 1.5 / * % Sim. to ISO 62
Water absorption, 2mm 4.7 / * % Sim. to ISO 62
Density 1490 / - kg/m³ ISO 1183
Density of melt 1290　kg/m³ -
Water Absorption, Immersion 24h 0.9 / * % ASTM D 570