PA66 103HSL NC010美國杜邦Zytel® 熱穩定潤滑聚酰胺66尼龍塑料注塑成型（18024445500）

Zytel® 103HSL NC010 is a heat stabilised, lubricated polyamide 66 resin for injection moulding.
General information Value Unit Test Standard
Resin Identification PA66 - -
Part Marking Code >PA66< - ISO 11469
RheologicalViscosity numberproperties 136dry[1]/ cond/* Unitcm³/g TestISO 307,Standard1157, 1628
Moulding shrinkage, parallel 1.3 / * % ISO 294-4, 2577
Moulding shrinkage, normal 1.3 / * % ISO 294-4, 2577
1: formic acid 90% 　 　 　
Mechanical properties dry/cond Unit Test Standard
Tensile Modulus 3100/1400 MPa ISO 527-1/-2
Yield stress 85/58 MPa ISO 527-1/-2
Yield strain 4.5/25 % ISO 527-1/-2
Nominal strain at break 20/>50 % ISO 527-1/-2
Strain at Break, 23°C, 50mm/min 40/- % ISO 527-1/-2
Flexural Modulus 2800/1200 MPa ISO 178
Tensile creep modulus 　 　 ISO 899-1
1h * / 1190 MPa 　
1000h * / 540 MPa 　
Charpy impact strength 　 　 ISO 179/1eU
23°C N / N kJ/m² 　
-30°C 400 / N kJ/m² 　
Charpy notched impact strength 　 　 ISO 179/1eA
23°C 5.5 / 12 kJ/m² 　
-30°C 4.5 / 3.5 kJ/m² 　
Izod notched impact strength 　 　 ISO 180/1A
23°C 5 / 10 kJ/m² 　
-30°C 6 / 5 kJ/m² 　
-40°C 5.5 / - kJ/m² 　
Izod impact strength 　 　 ISO 180/1U
23°C N/N kJ/m² 　
-30°C 300/N kJ/m² 　
Thermal properties dry/cond Unit Test Standard
Melting temperature, 10°C/min 262/* °C ISO 11357-1/-3
Glass transition temperature, 10°C/min 60/- °C ISO 11357-1/-2
Temp. of deflection under load 　 　 ISO 75-1/-2
1.8 MPa 70 / * °C 　
0.45 MPa 200 / * °C 　
Vicat softening temperature, 50°C/h, 50N 240 / * °C ISO 306
Coeff. of linear therm. expansion, parallel 100 / * E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 110 / * E-6/K ISO 11359-1/-2
Thermal conductivity of melt 0.16 W/(m K) -
Spec. heat capacity of melt 2790 J/(kg K) -
Eff. thermal diffusivity 5E-8 m²/s -
RTI, electrical 　 　 UL 746B
0.75 mm 140 / * °C 　
1.5mm 140 / * °C 　
RTI, impact 　 　 UL 746B
0.75 mm 95 °C 　
1.5mm 110 / * °C 　
RTI, strength 　 　 UL 746B
0.75 mm 115 °C 　
1.5mm 125 / * °C 　
Flammability dry / cond Unit Test Standard
Burning Behav. at 1.5mm nom. thickn. V-2 / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
UL recognition UL / * - -
Burning Behav. at thickness h V-2 / * class IEC 60695-11-10
Thickness tested 0.71 / * mm IEC 60695-11-10
Oxygen index 28 / * % ISO 4589-1/-2
Glow Wire Flammability Index 　 　 IEC 60695-2-1/2
0.75mm 850 / - °C 　
1.5mm 960 / - °C 　
3mm 960 / - °C 　
Glow Wire Ignition Temperature 　 　 IEC 60695-2-1/3
0.75mm 725/- °C 　
1.5mm 725/- °C 　
3mm 725/- °C 　
Electrical properties dry/cond Unit Test Standard
Relative permittivity 　 　 IEC 60250
100Hz 3.8 / 12.8 - 　
1MHz 3.5 / 4 - 　
Dissipation factor 　 　 IEC 60250
100Hz 75/5800 E-4 　
1MHz 165/700 E-4 　
Volume resistivity 1E13/1E11 Ohm*m IEC 60093
Electric strength 31/28 kV/mm IEC 60243-1
Comparative tracking index 　 　 　
Comparative tracking index 600 / - - IEC 60112
3.0mm 0 / - PLC UL 746A
Dielectric Constant 　 　 ASTM D 150
1 MHz 3.5 / - - 　
100 Hz 3.6 / - - 　
Surface Resistivity 1E12 / - Ohm ASTM D 257
Other properties dry / cond Unit Test Standard
Humidity absorption, 2mm 2.6 / * % Sim. to ISO 62
Water absorption, 2mm 8.5 / * % Sim. to ISO 62
Density 1140 / - kg/m³ ISO 1183
Density of melt 980 kg/m³ -
Film Properties dry / cond Unit Test Standard
Strain at yield, parallel 4.5 / * % ISO 527-3
VDA Properties Value Unit Test Standard
Emission of organic compounds 2.1 µgC/g VDA 277
Odour 2.5 class VDA 270