PA66 1200 A UV White 205美國普立萬聚酰胺66尼龍塑料(18024445500)
Technical Properties 1
Physical Typical Value(English) Typical Value (SI) Test Method
Specific Gravity 1.14 1.14 g/cm³ ASTM D792
Molding Shrinkage - Flow 0.018 to 0.024 in/in 1.8 to 2.4 % ASTM D955
WaterAbsorption (24 hr, 0.125 in (3.18 mm)) 1.2 % 1.2 % ASTM D570
Mechanical Typical Value(English) Typical Value (SI) Test Method
Tensile Modulus 430000psi 2960 MPa ASTM D638
Tensile Strength2 (Yield) 11500 psi 79.3 MPa ASTM D638
Tensile Strength2 (Break) 10200 psi 70.3 MPa ASTM D638
Tensile Elongation2 (Yield) 30% 30 % ASTM D638
Flexural Modulus 420000psi 2900 MPa ASTM D790
Flexural Strength 17000 psi 117 MPa ASTM D790
Impact Typical Value(English) Typical Value (SI) Test Method
Notched Izod Impact - Across Flow ASTM D256A
73°FInjection(23°C),Molded0.125 in (3.18 mm), 0.90 ft·lb/in 48 J/m
Thermal Typical Value(English) Typical Value (SI) Test Method
Deflection Temperature Under Load ASTM D648
264(3.18psimm)(1.8 MPa), Unannealed, 0.125 in 155 °F 68.3 °C
Melting Temperature 500 °F 260 °C ASTM D789
Additional Information
Molded Test Bars: Dry as Molded
Processing Information
Injection Typical Value(English) Typical Value (SI)
Drying Temperature 180 °F 82.2 °C
Drying Time 4.0 hr 4.0 hr |