PA66 AKV 35 HR H2.0 901510德國朗盛Durethan 35%玻纖熱老化穩(wěn)定水解穩(wěn)定尼龍66塑料（18024445500）

PA 66, 35 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 66, GHRW, 14-110, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 0.38　
C Molding shrinkage, transverse 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 1.05　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.06　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.09　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11500 7800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 195 135
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.1 6.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 85 85
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 75 80
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 13 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 75　
Izod impact strength -30 °C kJ/m² ISO 180-1U 65　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 <10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 10700 7000
Flexural strength 2 mm/min MPa ISO 178-A 305 210
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.8 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　180